Virgin Plastic Granules (HDPE/LDPE/LLDPE)

Home » Products » Virgin Plastic Granules (HDPE/LDPE/LLDPE)
Virgin Plastic Granules (HDPE/LDPE/LLDPE)

Compliant with ISO/SGS standards, our virgin plastic granules are manufactured from HDPE, LDPE or LLDPE, and they fit for film production, injection molding, extrusion molding and other uses. Aside from reliable quality and competitive price, our plastic pellet boasts many other outstanding properties as illustrated below.

Feature
1. Due to its good transparency, no discoloration, high tensile strength, high retraction ratio and excellent self-adhesive property, 1-meter-long wrap film made from LLDPE plastic granules are capable of packing objects whose length is 3-5 meters.

2. The virgin plastic granule is commonly adopted to produce packing films, and these films are non-toxic and highly resistant to tear, puncture, water, moisture, dust, corrosion and high temperature.

3. With the help of three-layer common-extruding machines, our recycled plastic granule could be made into pallet warp films (or LLDPE stretch films) so as to protect the surface of packed products, and this method saves both packaging and labor cost. Moreover, these films are easy to use and remove, and they are particularly suitable for palletized packaging.

Film Grade LLDPE
Test Value Unit
Melt Flow Rate (MFR) 2.0±0.4 g/10 min
Density 920±2 kg/cm3
Tensile Strength at Yield ≥8 MPa
Tensile Strength at Break ≥12 MPa
Haze ≤15 %
Packing 25 kg PP woven bags and then 20MT/20' FCL
LLDPE as Master Batch
Test Value Unit
Melt Flow Rate (MFR) 20 g/10 min
Density 0.924 g/cm3
Tensile Strength MD 12 MPa
TD 10
Elongation at Yield 13 %
Elongation at Break 200
Dark Drop Impact 105 g
Brittle Temperature (F50) -70
Vicat Softening Point 90
Packing 25 kg PP woven bags and then 20MT/20' FCL
LLDPE as Master Batch (Injection Molding)
Test Value Unit
Melt Flow Rate (MFR) 3.2 g/10 min
Density 0.939 g/cm3
Melting Point 127
Tensile Strength at Yield 21 MPa
Tensile Strength at Break 28 MPa
Elongation at Break 1,100 %
Flexural Modulus 750 MPa
Brittle Temperature <-60

Application
1. UFiber: Carpet, textile upholstery, etc.
2. Film: Shopping bag, casting film, multilayer film, etc.
3. Blow molding: Containers for medical, cosmetic, lubricant, paint, etc.
4. Extrusion molding: Sheet, pipe, wire, cable, etc.
5. Injection molding: Construction, houseware, furniture, toy, automotive parts, electronic products, etc.

Delivery: Within 2 weeks after receiving advance payment